GC-009 HI-QUALITY CARBONIZED FIBER IMPREGNATED GRAPHITE PTFE PACKING
The carbonized fiber yarn is treated with graphite particles, and then is braided to
form packing. Its surface is coated with a high-temperature-proof lubricant. It is able to bear high temperature
and pressure, and helps prevent abrasion and also help to minimize the effects of electrolytic pitting of the
valve stem.
| |
 |
| Presure |
Mpa |
3 |
25 |
25 |
| Temperature |
°C |
<650 |
| Line speed |
M/s |
20 |
2 |
2 |
| PH range |
0~14 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
- |
0.08 |
0.16 |
0.25 |
0.34 |
0.49 |
0.65 |
0.98 |
1.37 |
1.86 |
2.48 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-010 CARBON FIBER PTFE PACKING
It is braided packing made of carbon fiber which is impregnated with PTFE dispersion.
It is inert to almost all corrosive chemicals. When it is used for pumps, frictional heat is freely conducted to
the stuffing box metal because of its excellent thermal conductivity, and thus no damage will be caused to the
packing. It can replace PTFE asbestos packing within wide service range. It can be used to seal corrosive fluids
except strong oxidizer acids, organic solvents, fluids where contamination is not permissible for centrifugal
pumps, plunger pumps, mixers valves, etc.
| |
|
| Presure |
Mpa |
2 |
10 |
10 |
| Temperature |
°C |
<300 |
| Line speed |
M/s |
4 |
2 |
2 |
| PH range |
0~14 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
- |
0.08 |
0.15 |
0.23 |
0.32 |
0.47 |
0.60 |
0.90 |
1.26 |
1.70 |
2.30 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-011 Graphite PTFE GRAPHITE YARN AND BLENDED WITH SILICONE RUBBER CORE AT CENTRAL
positions, having excellent compression-compensating power. The applications are the same as GC-012
| |
|
| Presure |
Mpa |
3 |
10 |
20 |
| Temperature |
°C |
-200~280 |
| Line speed |
M/s |
0~20 |
| PH range |
0~14 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.075 |
0.15 |
0.23 |
0.33 |
0.50 |
0.63 |
0.83 |
1.22 |
1.70 |
2.39 |
3.10 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-012 GRAPHITE PTFE PACKING WITH OIL
It is braided packing made of PTFE yarn containing graphite and anti-corrosive
lubricant. It is recommended for shafts for almost all chemicals. Stability and long service lift are achieved
by low friction coefficient. It has great fear strength and high thermal conductivity. This self-lubrication
packing does not score the shaft and minimizes sleeve replacement cost. It can be used to seal alkalis, solvents,
water, steam, acids except strong oxidizing acids (aqua regia, fuming nitric acid, fuming nitric acid, fuming
sulfuric acid, etc.) for centrifugal pumps, autoclaves, agitators, mixers, etc.
| |
|
| Presure |
Mpa |
2 |
20 |
25 |
| Temperature |
°C |
-240~288 |
| Line speed |
M/s |
16 |
2 |
2 |
| PH range |
0~14 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.06 |
0.12 |
0.17 |
0.30 |
0.48 |
0.58 |
0.78 |
1.15 |
1.65 |
2.20 |
3.84 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-013 ARAMID FIBER PTFE PACKING
It is braided packing made of Aramid Fiber yarns impregnated with PTFE dispersion
and treated with lubricant. This packing can bear higher-pressure applications than tother types of braided
packing. Due to its steel-like strength, this yarn can be employed separately or as back-up rings with other
types of packing. This packing has been developed to replace asbestos packing for pump systems. It covers
all the service ranges which asbestos packing provides and even much better. It affords longer service life
under severe conditions which conventional asbestos packing can not provide satisfaction, such as sand
sultry, feed water pump of power stations, etc.
| |
|
| Presure |
Mpa |
3 |
20 |
20 |
| Temperature |
°C |
-100~280 |
| Line speed |
M/s |
25 |
15 |
2 |
| PH range |
2~13 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.06 |
0.12 |
0.20 |
0.29 |
0.42 |
0.57 |
0.74 |
1.14 |
1.65 |
2.19 |
2.85 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-014 GRAPHITE PTFE WITH ARAMID FIBER IN CORNERS REINFORCED BRAIDED PACKING
It is high quality braided packing made of PTFE yarns fiber with
incorporated graphite and the reinforced corner yarns of Aramid fiber. It can presence of high pressure and
temperature. It has good sliding velocity and thermal conductivity. It enables to seal high pressure piston
pump during a long running period. It can be used seal water, sewage water, hot water, oils, Greases, weak
acids and alkaline solutions, abrasive medium.
| |
|
| Presure |
Mpa |
2 |
20 |
25 |
| Temperature |
°C |
<280 |
| Line speed |
M/s |
20 |
2 |
2 |
| PH range |
2~12 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
- |
- |
0.22 |
0.33 |
0.45 |
0.63 |
0.83 |
1.39 |
1.87 |
2.48 |
3.24 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-015 PTFE WITH ARAMID FIBER IN CORNERS REINFORCED BRAIDED PACKING
It is braided packing made of PTFE yarns fiber and the reinforced
corner yarns of Aramid fiber. This structure enhances the lubricability of Aramid fiber and reinforces the
strength of the pure PTFE packing. This special combination packing play a very important role in the sealing
of high pressure piston pump.
| |
|
| Presure |
Mpa |
2 |
20 |
25 |
| Temperature |
°C |
<280 |
| Line speed |
M/s |
12 |
2 |
2 |
| PH range |
2~13 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
- |
- |
0.22 |
0.33 |
0.45 |
0.63 |
0.83 |
1.39 |
1.87 |
2.48 |
3.24 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-016 RAMIE PACKING WITH VASELINE
Made through braiding of basic material ramie filament, Impregnated with Vaseline
and shaping, highly wearing-resistant, an ideal substitute for asbestos packings, especially applicable of
ship industry.
| |
|
| Presure |
Mpa |
5 |
8 |
0 |
| Temperature |
°C |
-50 ~ 130 |
| Line speed |
M/s |
0~10 |
| PH range |
4~12 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.06 |
0.12 |
0.21 |
0.31 |
0.42 |
0.56 |
0.70 |
1.12 |
1.62 |
2.05 |
2.85 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-017 ACRYLIC PACKING WITH PTFE
Made of polyacrylonitrile filament through reinforcing, braiding
and impregnated with PTFE, having high strength, wear-and impact-resistance, an ideal substitute for asbestos
packing, and applicable for packing seal of pumps, valves and vessels at a high linear speed and pressure.
| |
|
| Presure |
Mpa |
5 |
10 |
20 |
| Temperature |
°C |
-100 ~ 250 |
| Line speed |
M/s |
0~12 |
| PH range |
4~10 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.05 |
0.10 |
0.18 |
0.27 |
0.37 |
0.51 |
0.65 |
1.02 |
1.46 |
1.98 |
2.62 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|
GC-018 ACRYLIC PACKING WITH PTFE
Made of polyacrylonitrile filament through reinforcing, braiding
and impregnated with PTFE, having high strength, wear-and impact-resistance, an ideal substitute for asbestos
packing, and applicable for packing seal of pumps, valves and vessels at a high linear speed and pressure.
| |
|
| Presure |
Mpa |
5 |
10 |
20 |
| Temperature |
°C |
-100~250 |
| Line speed |
M/s |
0~12 |
| PH range |
4~10 |
| Standard Size(inch) |
3.2(1/8) |
4.8(3/16) |
6.4(1/4) |
7.9(5/16) |
9.5(3/18) |
11.1(7/16) |
12.7(2/1) |
15.9(5/8) |
19.9(3/4) |
22.2(7/8) |
25.4(1) |
| Kg/3m |
0.05 |
0.10 |
0.18 |
0.27 |
0.37 |
0.51 |
0.65 |
1.02 |
1.46 |
1.98 |
2.62 |
| Braiding Method |
Square Braid |
Lattice Braid |
|
|